A novel β-nucleating agent for isotactic polypropylene
|
|
|
|
|
نویسنده
|
Chunmeng Pan ,Wei Qin ,Lan Chen ,Zhong Xin ,Shicheng Zhao ,Chunlin Ye
|
منبع
|
journal of thermal analysis and calorimetry - 2018 - دوره : 134 - شماره : 3 - صفحه:2029 -2040
|
چکیده
|
a series of metal salts of 7-oxabicyclo[2.2.1]hept-5-ene-2,3-dicarboxylic acid were synthesized, and their nucleation efficiency in isotactic polypropylene (ipp) was investigated. the results showed that potassium 7-oxabicyclo[2.2.1]hept-5-ene-2,3-dicarboxylate (obche19) is an effective β-nucleating agent. then, the effect of obche19 concentration on the relative content of β-crystals (kβ) and mechanical properties of ipp was investigated. the results indicated that the maximum kβ reached 0.82 and impact strength increased by 125% compared to that of pure ipp when the content of obche19 is 0.1 mass%. furthermore, the non-isothermal crystallization kinetics and crystallization activation energy were investigated by the caze method and kissinger method, respectively.
|
کلیدواژه
|
Isotactic polypropylene ,Nucleating agent ,OBCHED ,Crystallization ,Mechanical properties
|
آدرس
|
East China University of Science and Technology, Shanghai Key Laboratory of Multiphase Materials Chemical Engineering, Department of Product Engineering, China, East China University of Science and Technology, Shanghai Key Laboratory of Multiphase Materials Chemical Engineering, Department of Product Engineering, China, East China University of Science and Technology, Shanghai Key Laboratory of Multiphase Materials Chemical Engineering, Department of Product Engineering, China, East China University of Science and Technology, Shanghai Key Laboratory of Multiphase Materials Chemical Engineering, Department of Product Engineering, China, East China University of Science and Technology, Shanghai Key Laboratory of Multiphase Materials Chemical Engineering, Department of Product Engineering, China, Shanghai Research Institute of Chemical Industry, China
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|