EFFECT OF BORONIZING SURFACE TREATMENT ON THE ADHESIVE WEAR BEHAVIOR OF FERRITIC-PEARLITIC DUCTILE IRON
|
|
|
|
|
|
|
|
نویسنده
|
GÜL Ferhat
|
|
منبع
|
journal of the faculty of engineering and architecture of gazi university - 2010 - دوره : 25 - شماره : 2 - صفحه:389 -395
|
|
چکیده
|
In this study, effect of boronizing surface treatment on adhesive wear behavior of ferritic-pearlitic ductile iron was studied. boronizing was performed in ekabor ii boronizing agent at 960 ºc for 6 hours. adhesive wear test was performed on pin on disc type wear tester under the load of 60 n, at sliding speed of 1 m/s for 3600 m, 7200 m ve 10800 m ve 21600 m sliding distance. adhesive wear test results show that, wear resistance of boronized ductile iron is 50 times higher than those of ferritic-pearlitic ductile iron as-cast.
|
|
کلیدواژه
|
Ductile iron ,boronizing ,wear
|
|
آدرس
|
Gazi Üniversitesi, Teknik Egitim Fakültesi, Döküm Egitimi ABD, Turkey
|
|