   Fatigue strength of Ce-TZP/Al2O3 nanocomposite with different surfaces  
   
نویسنده takano t. ,tasaka a. ,yoshinari m. ,sakurai k.
منبع journal of dental research - 2012 - دوره : 91 - شماره : 8 - صفحه:800 -804
چکیده    Ce-tzp/al2o3 nanocomposite (nanozr) has not only higher strength,but also higher fracture toughness than conventional y-tzp,indicating its potential for use in dental implants. surface treatment to obtain osseointegration,however,may alter its surface topography,thus affecting the cyclic fatigue strength that plays such an important role in the durability of this material. the aim of this study was to evaluate the influence of surface treatment on cyclic fatigue strength in nanozr as compared with grit-blasted and acid-etched y-tzp (125be y-tzp). bi-axial flexure strength was measured in both static and cyclic fatigue tests,as recommended by iso 6872. the cyclic fatigue test was performed by the staircase method in distilled water at 37°c,with a load of 106 cycles and 10 hz. bi-axial flexure strength of nanozr was 1111-1237 mpa and 667-881 mpa in the static and cyclic fatigue tests,respectively. the bi-axial flexure strength of nanozr under all conditions was greater than that of 125be y-tzp in the static and cyclic fatigue tests. the cyclic fatigue strength of nanozr was more than twice that of y-tzp as specified in iso 13356 for surgical implants (320 mpa),indicating the promise of this material for use in dental implants. © 2012 international & american associations for dental research.
کلیدواژه bi-axial flexure strength; dental composite; dental implant; dental restorations; surface treatment; zirconia
آدرس division of oral implants research,oral health science center,tokyo dental college,1-2-2,masago,mihama-ku,chiba 261-8502,japan,department of removable prosthodontics and gerodontology,tokyo dental college,mihama-ku,chiba, Japan, division of oral implants research,oral health science center,tokyo dental college,1-2-2,masago,mihama-ku,chiba 261-8502,japan,department of removable prosthodontics and gerodontology,tokyo dental college,mihama-ku,chiba, Japan, division of oral implants research,oral health science center,tokyo dental college,1-2-2,masago,mihama-ku,chiba 261-8502, Japan, department of removable prosthodontics and gerodontology,tokyo dental college,mihama-ku,chiba, Japan
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved