   Micro-sized erosions in a nanofilled composite after repeated acidic beverage exposures: Consequences of clusters dislodgments  
   
نویسنده svizero n.r. ,góes a.r.c.g. ,bueno t.l. ,di hipólito v. ,wang l. ,d'alpino p.h.p.
منبع journal of applied oral science - 2014 - دوره : 22 - شماره : 5 - صفحه:373 -381
چکیده    Objective: to evaluate the hardness (khn),color stability (δe),and superficial micromorphology of two categories of composites after immersion in either distilled water or grape juice for up to 45 days. material and methods: cylindrical specimens (6 mm diameter x 2 mm thick) were obtained according to the factors: composite [opallis (fgm) and filtek z350xt (3m espe)]; immersion solution (distilled water and grape juice); and evaluation time: 24 h and 7,14,21,28,and 45 days. after photoactivation,the specimens were stored at 37°c for 24 h. khn (50 g/15 s) and δe were then repeatedly assessed according to the immersion solutions. data were analyzed (three-way anova/tukey's test). scanning electron microscopy (sem) topographic analysis was also performed. results: in general,khn of both composites reduced after 24 h,irrespective of the immersion solution and time. a significantly lower khn was noted for opallis compared with filtek z350xt in all parameters. an increase in δe over time was noted for both composites,irrespective of the immersion solution. significantly higher ae was noted for filtek z350xt immersed in grape juice compared with opallis,regardless of the evaluation time. the grape juice caused significantly higher δe compared with water in all periods. sem analysis showed eroded areas for filtek z350xt but not for opallis. conclusions: the compositions and immersion solutions influence the composite hardness and the color stability. in spite of the higher hardness,the nanofilled composite is more susceptible to color change than the microhybrid when immersed in an acidic dyed solution. © 2014,faculdade de odontologia de bauru. all rights reserved.
کلیدواژه Color; Composite resins; Hardness; Time factor
آدرس hospital for rehabilitation of craniofacial anomalies (hrac-usp),university of são paulo,bauru,sp, Brazil, department of operative dentistry,endodontics and dental materials,bauru school of dentistry,university of são paulo,bauru,sp, Brazil, department of operative dentistry,endodontics and dental materials,bauru school of dentistry,university of são paulo,bauru,sp, Brazil, biomaterials research group,universidade anhanguera de são paulo (unian-sp),são paulo,sp, Brazil, department of operative dentistry,endodontics and dental materials,bauru school of dentistry,university of são paulo,bauru,sp, Brazil, biomaterials research group,universidade anhanguera de são paulo (unian-sp),são paulo,sp, Brazil
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved