   Effects of Cast Extrusion Line Speed on the Crystallinity of Lldpe Stretch Films  
   
نویسنده Yadegari Ali ,Bayazian Hoda ,Schöppner Volker
منبع كنفرانس بين المللي دوسالانه نفت، گاز و پتروشيمي - 1399 - دوره : 3 - سومین دوره کنفرانس بین المللی دوسالانه نفت، گاز و پتروشیمی - کد همایش: 99200-29885 - صفحه:1 -8
چکیده    Influence of line speed on the crystallinity of linear low density polyethylene (lldpe) stretch films manufactured in a cast extrusion line was examined using differential scanning calorimetry (dsc) and wide angle x-ray diffraction (waxd). the multilayer lldpe films were prepared at wide range of line speeds from 200 to 1000 m/min. the dsc results showed that there is an increase in the crystallinity of films at higher line speeds. furthermore, evaluating melting endotherms indicated that the size of crystals was more uniform as the line speed increased. crystallinity of films obtained from waxd analysis also exhibited the similar trend of dsc results, though their values were different. in addition, there was a reduction in crystal size calculated from waxd data upon increasing the line speed. the observed increase in crystallinity and decrease in crystal size was due to enhanced flow induced crystallization (fic) as a result of greater shear stresses the polymer melt encountered at higher line speeds.
کلیدواژه Lldpe ,Cast Film ,Crystallinity ,Dsc ,Waxd
آدرس Persian Gulf University, Faculty Of Petroleun, Gas And Petrochemical Engineering, Universität Paderborn, Universität Paderborn
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved