Investigation of Shielding Gas Composition on Formation of Porosity in Flux Core Arc Welding of A516 Gr70
|
|
|
|
|
DOR
|
20.1001.2.9515121601.1395.1.1.34.3
|
|
نویسنده
|
Sarabi Tabrizi Saeid
|
|
منبع
|
كنفرانس بين المللي پژوهش در نوآوري و فناوري - 1395 - دوره : 1 - اولین کنفرانس بین المللی پژوهش در نوآوری و فناوری - کد همایش: 95151-21601
|
|
|
|
|
چکیده
|
Porosity is one of the main problems in welding of a516gr70 through flux core arc welding (fcaw); therefore, this paper is sought to investigate the effect of shielding gas composition on the rate of porosity and four modes of gas composition are considered for this investigation which include: in order to prove the validity of experiment, three samples are considered for each one of compositions that are totally 12 (4*3) and metal a516 gr 70 with a thickness of 10 mm was also selected for samples.
|
|
کلیدواژه
|
Flux Cored Arc Welding ,Gas Composition: ,The Composition Of Argon And Co2 ,Ultrasonic Welding Test ,Argon ,Carbon Dioxide (Co2)
|
|
آدرس
|
Master'S Degree In Materials Engineering - Welding Department, Iran
|
|
پست الکترونیکی
|
s_sarabi_t@yahoo.com
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Investigation of shielding gas composition on formation of porosity in flux core arc welding of A516 Gr70
|
|
|
|
|
Authors
|
Sarabi Tabrizi Saeid
|
|
Abstract
|
Porosity is one of the main problems in welding of A516Gr70 through flux core arc welding (FCAW); therefore, this paper is sought to investigate the effect of shielding gas composition on the rate of porosity and four modes of gas composition are considered for this investigation which include: In order to prove the validity of experiment, three samples are considered for each one of compositions that are totally 12 (4*3) and metal A516 Gr 70 with a thickness of 10 mm was also selected for samples.
|
|
Keywords
|
Flux Cored Arc Welding ,Gas Composition: ,The Composition Of Argon And CO2 ,Ultrasonic Welding Test ,Argon ,Carbon Dioxide (CO2)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|