the reduction of nitro compounds using nd2sn2o7 nanoceramic
|
|
|
|
|
|
|
|
نویسنده
|
khoshtabkh mostafa ,nobahari mahdi ,movahedifar mojtaba ,honarbakhsh amin ,zhiani rahele
|
|
منبع
|
iranian journal of analytical chemistry - 2024 - دوره : 11 - شماره : 1 - صفحه:69 -77
|
|
چکیده
|
Nd2sn2o7 nanoceramic was synthesized using an eco-friendly method with sncl4•5h2o and nd(no3)3•6h2o. structural analysis confirmed the formation of nd2sn2o7 nanoceramic with a size of 20±8 nm. nd2sn2o7 was thoroughly characterized using sem, xrd, tga, edx, and tem techniques. due to its high mechanical and long-term colloidal stability, large ionic character, and thermal stability, this system is considered an ideal nanocatalyst employing the host-guest approach. this green and environmentally friendly method was tested for the reduction of nitro-aromatic compounds using the synthesized nd2sn2o7 nanoceramic. the catalyst demonstrated easy and effective reusability after the reaction was completed under visible light irradiation.
|
|
کلیدواژه
|
nanoceramic ,green chemistry ,nd2sn2o7 ,nitro-aromatic compounds ,wastewater
|
|
آدرس
|
islamic azad university, neyshabur branch, department of civil engineering, iran, islamic azad university, neyshabur branch, new materials technology and processing reserearch center, department of civil engineering, iran, islamic azad university, neyshabur branch, new materials technology and processing reserearch center, department of civil engineering, iran, islamic azad university, neyshabur branch, new materials technology and processing reserearch center, department of civil engineering, iran, islamic azad university, neyshabur branch, new materials technology and processing reserearch center, advanced research center for chemistry, department of chemistry, iran
|
|
پست الکترونیکی
|
r_zhiani2006@yahoo.com
|
|
|
|
|
|
|
|
|
|
|
|
|
|
اهش ترکیبات نیترو با استفاده از نانوسرامیک nd2sn2o7
|
|
|
|
|
Authors
|
خوشبخت مصطفی ,نوبهاری مهدی ,موحدی فر سید مجتبی ,هنربخش امین ,زمانی راحله
|
|
Abstract
|
نانوسرامیک nd2sn2o7 با استفاده از یک روش سازگار با محیط زیست با sncl4•5h2o و nd(no3)3•6h2o سنتز شدند. تجزیه و تحلیل ساختاری تشکیل نانوسرامیک nd2sn2o7 با اندازه 8±20 نانومتر را تایید کرد. nd2sn2o7 به طور کامل با استفاده از تکنیک های sem، xrd، tga، edx و tem مشخص شد. این سیستم به دلیل پایداری کلوئیدی بالای مکانیکی و بلندمدت، ویژگی یونی بزرگ و پایداری حرارتی، یک نانوکاتالیست ایده‌آل با استفاده از رویکرد میزبان-میهمان در نظر گرفته می‌شود. این روش سبز و سازگار با محیط زیست برای کاهش ترکیبات نیترو-آروماتیک با استفاده از نانوسرامیک سنتز nd2sn2o7 مورد آزمایش قرار گرفت. کاتالیزور قابلیت استفاده مجدد آسان و موثر را پس از تکمیل واکنش تحت تابش نور مرئی نشان داد.
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|