optimization of nickel removal process from zinc sulfate solution using central composite design of experiments

Nickel is one of the metallic impurities that should be removed from the electrolyte solution before the electrowinning of zinc. this study investigated the parameters affecting the process of nickel removal in an iranian zinc smelter plant by the response surface methodology. according to the results of experiments, the optimum condition for removal of nickel was obtained at temperature of 85 °c, the residence time of 60 minutes, zinc powder of 2.5 g/l, mixing speed of 500 rpm, and ph of 5. with regards to the resulting model from the design-expert software, the significant parameters were concentration, residence time, and temperature, respectively.

بررسی و بهینه سازی پارامترهای موثر بر حذف نیکل از محلول سولفات روی با استفاده از طرح مرکب مرکزی

نیکل یکی از ناخاصی­های فلزی می­باشد که قبل از الکترووینینگ روی باید از محلول الکترولیت حذف شود. در این پژوهش پارامترهای موثر بر فرایند حذف نیکل در کارخانه روی دندی توسط روش سطح پاسخ مورد بررسی قرار گرفت. نتایج آزمایشات نشان داد که بهینه­ترین حالت برای حذف نیکل در دمای 85 درجه­سانتی­گراد، زمان ماند 60 دقیقه، 2.5 گرم بر لیتر غلظت پودر روی، اختلاط 500 دور بر دقیقه و pH برابر 5 حاصل شد. با توجه با مدل حاصله از نرم افزار دیزاین اکسپرت، بیشترین تاثیر گذاری به ترتیب متعلق به غلظت، زمان ماند و دما می­باشد.