   the effect of multi-walled carbon nanotubes, as the reinforcement phase, on the hardness and bending strength of aluminum alloy 7075  
   
نویسنده barati f. ,esfandiari m.
منبع journal of stress analysis - 2021 - دوره : 6 - شماره : 1 - صفحه:61 -66
چکیده    In the present investigation, to fabricate nanocomposites made of wrought aluminum alloy 7075 and multi-walled carbon nanotubes, carbon nanotubes and the alloy powders were initially dispersed in ethanol using an ultrasonic shaker to form a primary mixture. the milled powder mixture was converted into the final specimens by spark-plasma sintering. to achieve a uniform distribution of carbon nanotubes in the matrix alloy, ethanol or stearic acid can be used as a processing control agent (pca). for each of the seven specimens, a series of tests were performed to study the effects of the reinforcement phase on the base alloy. as shown, the reinforced specimens were harder compared to the pure al7075 and the sample reinforced with 1wt% of multi-walled carbon nanotubes has both the highest hardness and flexural strength among all the specimens. additionally, when the weight fraction reached 2%, there was a noticeable drop in the mechanical properties. this novel alloy produced by powder metalurgy can be very helpul for industrial application where the increase in strength and hardness is deireable.
کلیدواژه high-energy ball mill ,multi-walled carbon nanotubes ,nanocomposites ,spark-plasma sintering
آدرس islamic azad university, hamedan branch, department of mechanical engineering, iran, islamic azad university, hamedan branch, department of mechanical engineering, iran
پست الکترونیکی esfandiarim3@gmail.com
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved