Synthesis and Luminescent Characteristics of Ce3+-Activated Borosilicate Blue-Emitting Phosphors for LEDs
|
|
|
|
|
|
|
|
نویسنده
|
yu h. ,chen j. ,gan s.
|
|
منبع
|
journal of spectroscopy - 2016 - دوره : 2016 - شماره : 0
|
|
چکیده
|
The phosphors sr3b2sio8:ce3+ have been successfully synthesized via solid-state reaction process. emission/excitation spectra and photoluminescence decay behaviors were investigated in detail. under the excitation of 340 nm,the emission spectrum presented an asymmetry emission band extended from 350 to 600 nm,which with the main peak at 425 nm can be fitted in two peaks (23940 cm-1 and 21934 cm-1). the chromaticity coordinates of sr3-xb2sio8:xce3+ are fixed in the blue region; when the intensity of ce3+ reached the maximum,the chromaticity coordinate is (0.154,0.088) which is more close to the standard cie of blue light (0.140,0.080). the results showed the kind of phosphor may have potential applications in the fields of uv-excited white leds. © 2016 hong yu et al.
|
|
|
|
|
آدرس
|
research institute for new materials technology,chongqing key laboratory of environmental materials and remediation technologies,chongqing university of arts and science,chongqing, China, college of materials and chemical engineering,chongqing university of arts and science,chongqing, China, college of chemistry,jilin university,changchun, China
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|