SEM-EDX analysis of laser surface alloying on aluminum
|
|
|
|
|
|
|
|
نویسنده
|
bidin n. ,abdullah m. ,shaharin m.s. ,alwafi y.a. ,riban d.g. ,yasin m.
|
|
منبع
|
journal of mathematical and fundamental sciences - 2013 - دوره : 45 - شماره : 1 - صفحه:53 -60
|
|
چکیده
|
Microstructure and chemical composition changes on the alloyed aluminum surface were investigated using sem-edx analysis. a q-switched nd:yag laser was focused to induce breakdown and plasma formation. the high plasma temperature and the shock wave pressure were responsible for speeding up the laser surface alloying process. the rapid heat and cooling process introduced a non-equilibrium condition causing changes in the microstructure as well as the chemical composition of the alloyed aluminum surface. the remelted layer and molten pools were realized after the aluminum received a power density greater than 5 × 108 wcm-2. the chemical composition change confirms that the convection process had taken place during the alloying process. © 2013 published by itb journal publisher.
|
|
کلیدواژه
|
Chemical composition; Fe-Cu powder; Intermetallics phase; Laser alloying; Microstructure
|
|
آدرس
|
advanced photonic science institute,university teknologi malaysia, Malaysia, advanced photonic science institute,university teknologi malaysia, Malaysia, advanced photonic science institute,university teknologi malaysia, Malaysia, advanced photonic science institute,university teknologi malaysia, Malaysia, ibnu sina institute for fundamental science studies,universiti teknologi malaysia,81310 utm skudai, Malaysia, advanced photonic science institute,university teknologi malaysia,skudai 81300,malaysia,department of physics,airlangga university,jalan mulyorejo, Indonesia
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|