Enhanced hydrogen storage capacity over electro-synthesized HKUST-1
|
|
|
|
|
|
|
|
نویسنده
|
lestari w.w. ,adreane m. ,suwarno h.
|
|
منبع
|
journal of mathematical and fundamental sciences - 2017 - دوره : 49 - شماره : 3 - صفحه:213 -224
|
|
چکیده
|
Hkust-1 [cu3(1,3,5-btc)2] (btc = benzene-tri-carboxylate) was synthesized using an electrochemical method and tested for hydrogen storage. the obtained material showed a remarkably higher hydrogen uptake over reported hkust-1 and reached until 4.75 wt% at room temperature and low pressure up to 1.2 bar. this yield was compared to hkust-1 obtained from the solvothermal method,which showed a hydrogen uptake of only 1.19 wt%. enhancement of hydrogen sorption of the electro-synthesized product was due to the more appropriate surface area and pore size,effected by the preferable physical interaction between the hydrogen gasses and the copper ions as unsaturated metal centers in the frameworks of hkust-1. © 2017 published by itb journal publisher.
|
|
کلیدواژه
|
Copper(II); Electrosynthesis; H3BTC; HKUST-1; Hydrogen storage; Solvothermal
|
|
آدرس
|
research group of porous materials for sustainability,department of chemistry,faculty of mathematics and natural sciences,sebelas maret university,jalan ir. sutami no. 36a,kentingan-jebres,surakarta, Indonesia, research group of porous materials for sustainability,department of chemistry,faculty of mathematics and natural sciences,sebelas maret university,jalan ir. sutami no. 36a,kentingan-jebres,surakarta, Indonesia, center for nuclear fuel technology,batan,serpong, Indonesia
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|