   Comparison of corrosion behavior of electrochemically deposited nano-cobalt-coated Ni sheet  
   
نویسنده al-aqeeli n. ,toor i.-u.-h.
منبع journal of chemistry - 2013 - دوره : 2013 - شماره : 0
چکیده    Corrosion behavior of nano-coblat-coated ni sheet was compared with pure ni and 20% fe-ni alloy sheet using potentiodynamic polarization and linear polarization technique in 0.1 m nacl solution at room temperature. results showed that corrosion resistance properties of nano-co-coated ni sheet were almost same as that of pure ni sheet,however corrosion resistance of 20% fe-ni sheet was decreased significantly. pitting potential of 20% fe-ni sheet was subsequently decreased as compared to pure ni sheet as well as nano-cobalt-coated ni sheet. sem/eds analysis of the corroded surfaces showed that both pure ni and nano-coblat-coated ni sheet did not show any appreciable corrosion however significant corrosion was observed in the case of 20% fe-ni sheet. © 2013 nasser al-aqeeli and ihsan-ul-haq toor.
آدرس deptartment of mechanical engineering,king fahd university of petroleum and minerals (kfupm), Saudi Arabia, deptartment of mechanical engineering,king fahd university of petroleum and minerals (kfupm), Saudi Arabia
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved