Study of flow-assisted corrosion of AZ91D magnesium alloy in loop system based on array electrode technology
|
|
|
|
|
|
|
|
نویسنده
|
huang h. ,zhang g. ,yang j. ,pan z. ,guo x.
|
|
منبع
|
journal of chemistry - 2015 - دوره : 2015 - شماره : 0
|
|
چکیده
|
A loop system was used to investigate flow-assisted corrosion (fac) of az91d magnesium alloy at an elbow based on array electrode technology by potentiodynamic polarization,computational fluid dynamics,simulation and surface analysis. the experimental results demonstrate the fluid hydrodynamics plays a significant role in the fac of az91d magnesium alloy. the corrosion rate increases from the outer wall to the inner wall of the elbow,with the higher corrosion rate corresponding to the higher flow velocity and larger shear stress at the elbow. the maximum corrosion rate appears at the innermost wall of the elbow,the location with the maximum flow velocity and shear stress. © 2015 hualiang huang et al.
|
|
|
|
|
آدرس
|
hubei key laboratory of materials chemistry and service failure,school of chemistry and chemical engineering,huazhong university of science and technology,wuhan,china,school of chemistry and environmental engineering,wuhan institute of technology, China, hubei key laboratory of materials chemistry and service failure,school of chemistry and chemical engineering,huazhong university of science and technology, China, hubei key laboratory of materials chemistry and service failure,school of chemistry and chemical engineering,huazhong university of science and technology, China, school of chemistry and environmental engineering,wuhan institute of technology, China, hubei key laboratory of materials chemistry and service failure,school of chemistry and chemical engineering,huazhong university of science and technology, China
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|