   Fcc Catalyst Attrition Behavior At High Temperatures  
نویسنده Foroutan Ghazvini Saba ,Afshar Ebrahimi Ali ,Jafarnia Hadi
منبع Journal Of Particle Science And Technology - 2019 - دوره : 5 - شماره : 4 - صفحه:135 -143
چکیده    In this work, high temperature attrition was studied in a standard attrition set-up to mimic the fcc regenerator environment with mechanical attrition. operating conditions were modified in this pilot due to the application of high temperatures. two parameters, i.e., time and temperature in the ranges of 1 to 5h and 673-973k, were surveyed, respectively. the behavior of attrition and mass loss was then modeled and validated. at higher temperatures mass loss response sensitivity became larger. finally, psd and sem tests were used to investigate the attrition mechanism. in the ambient tests, abrasion was significant while at higher temperatures, fragmentation was considerable. psd plots shifted into larger particles and sem images showed those changes as well. in addition, significant reshaping in the psd curves indicated particle cracking at high temperatures.
کلیدواژه Fcc Catalyst Particles ,Attrition ,High Temperature ,Rsm ,Psd
آدرس Iran Polymer And Petrochemical Institute, Faculty Of Petrochemicals, Iran, Iran Polymer And Petrochemical Institute, Faculty Of Petrochemicals, Iran, Arak Oil Refinery, Process Engineering Department, Iran
پست الکترونیکی seyedhadi.jafarnia@gmail.com

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved