   Enhancement of E-Glass Fiber/Epoxy Composite Bending Performance Via Graphene Addition  
   
نویسنده Imanparast Mohammad ,Khosravi Hamed
منبع Journal Of Particle Science And Technology - 2020 - دوره : 6 - شماره : 2 - صفحه:61 -65
چکیده    This paper presents an experimental investigation using graphene nanoplatelets (gnps) to enhance the bending performance of e-glass fiber/epoxy composites. each specimen was prepared with two layers of e-glass chopped strand mat via the hand lay-up technique and using various contents of gnps in the matrix (0.1, 0.2, 0.3, 0.4 and 0.5 wt%). mechanical and ultrasonic stirring methods were employed to disperse the gnps in the matrix. the obtained results demonstrated that the highest increases of 23% and 26% in the flexural strength and modulus, respectively, were observed for the composite containing 0.4 wt% gnps. with the incorporation of 0.1 wt% gnps, the flexural failure strain of the composite was enhanced by 16% compared to the control composite. the evaluation of the fractured surfaces clearly demonstrated that the interface between the glass fiber and polymeric matrix was improved when gnps were added into the matrix.
کلیدواژه Fiber-Reinforced Composite ,Graphene Nanoplatelets ,Bending Performance ,Fracture Surface
آدرس University Of Sistan And Baluchestan, Faculty Of Engineering, Department Of Mechanical Engineering, Iran, University Of Sistan And Baluchestan, Faculty Of Engineering, Department Of Materials Engineering, Iran
پست الکترونیکی hkhosravi@eng.usb.ac.ir
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved