Thermo-Mechanical Treatment of Alcocrfeni2.1 High-Entropy Alloy
|
|
|
|
|
نویسنده
|
Erfani Mobarakeh S.A. ,Dehghani K.
|
منبع
|
Iranian Journal Of Materials Forming - 2022 - دوره : 9 - شماره : 1 - صفحه:41 -46
|
|
|
چکیده
|
In this study, the microstructural evolutions, formed phases, micro- and macro-hardness changes and shear properties were evaluated in the as-cast, homogenized, cold-rolled and annealed alcocrfeni2.1 eutectic high-entropy alloy (ehea). these studies were carried out using x-ray fluorescence (xrf), scanning electron microscopy (sem), rockwell c and vickers hardness testing as well as shear punch testing (spt). the microstructure after cold rolling followed by annealing was consisted of an elongated phases/grains in the direction of cold rolling and in almost equiaxed phases/grains. the homogenized specimen has the minimum amounts of hardness and yield/ultimate shear strength. due to the presence of both elongated and equiaxed structures in the cold-rolled and annealed sample, the hardness and yield/ultimate shear strength of this specimen is between that of as-cast and homogenized cases
|
کلیدواژه
|
Eutectic High-Entropy Alloy (Ehea) ,Cold Rolling ,Annealing ,Hardness ,Shear Punch Test (Spt)
|
آدرس
|
Amirkabir University Of Technology (Tehran Polytechnic), Department Of Materials And Metallurgical Engineering, Iran, Amirkabir University Of Technology (Tehran Polytechnic), Department Of Materials And Metallurgical Engineering, Iran
|
پست الکترونیکی
|
dehghani@aut.ac.ir
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|