hot workability and processing map of high gd content mg-gd-zn-zr-nd alloy
|
|
|
|
|
|
|
|
نویسنده
|
mosadegh s. ,aghaie-khafri m. ,binesh b.
|
|
منبع
|
iranian journal of materials forming - 2021 - دوره : 8 - شماره : 2 - صفحه:44 -53
|
|
چکیده
|
Hot workability of as-extruded high gd content mg-5gd-0,5zn-0.5zr-2.5nd alloy was investigated using the hot compression test in a temperature range of 300-500°c and strain rates of 0.001-1s^-1. hot workability assessment was conducted by capturing microstructural evolution of high temperature deformed samples, and by constructing power dissipation and instability maps. using experimental data of hot compression tests, the power dissipation map of the alloy was constructed, in which a domain of dynamic recrystallization (drx) occurred at the temperature range of 350-450°c and strain rate of 0.001-0.1 s^-1, representing the optimum hot working window. furthermore, the processing map of the alloy was constructed, and flow instability regions were also indicated based on the ziegler's flow instability criterion
|
|
کلیدواژه
|
magnesium alloy ,rare earth metals ,processing map ,hot workability
|
|
آدرس
|
k. n. toosi university of technology, faculty of materials science and engineering, iran, k. n. toosi university of technology, faculty of materials science and engineering, iran, university of bonab, department of materials science and engineering, iran
|
|
پست الکترونیکی
|