MICROSTRUCTURE CHARACTERIZATION OF WCCo-Mo BASED COATINGS PRODUCED USING HIGH VELOCITY OXYGEN FUEL
|
|
|
|
|
|
|
|
نویسنده
|
ISLAK Serkan ,KIR Durmuş ,BUYTOZ Soner ,ÖZORAK Cihan ,AKKAŞ Mehmet ,ÇALIGÜLÜ Uğur ,YILDIRIM M. Mustafa
|
|
منبع
|
pamukkale university journal of engineering sciences - 2015 - دوره : 21 - شماره : 8 - صفحه:344 -347
|
|
چکیده
|
The present study has been carried out in order to investigate the microstructural properties of wcco-mo composite coatings deposited onto a sae 4140 steel substrate by high velocity oxygen fuel (hvof) thermal spray. for this purpose, the mo quantity added to the wcco was changed as 10, 20, 30 and 40 wt. % percents. the coatings are compared in terms of their phase composition, microstructure and hardness. phase compound and microstructure of coating layers were examined using x-ray diffractometer (xrd) and scanning electron microscope (sem). xrd results showed that wcco-mo composite coatings were mainly composed of wc, w2c, co3w3c, mo2c, moo2, mo and co phases. the average hardness of the coatings increased with increasing mo content.
|
|
کلیدواژه
|
Mo ,WCCo ,HVOF ,Microstructure ,Hardness
|
|
آدرس
|
Kastamonu Üniversitesi, Mühendislik-Mimarlık Fak, Malzeme Bilimi ve Nanoteknoloji Mühendisliği Bölümü, Türkiye, Kocaeli Üniversitesi, Hereke Meslek Yüksekokulu, Türkiye, Fırat Üniversitesi, Teknoloji Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümü, Turkey, Kastamonu Üniversitesi, Mühendislik-Mimarlık Fak, Malzeme Bilimi ve Nanoteknoloji Mühendisliği Bölümü, Türkiye, Kastamonu Üniversitesi, Cide Rıfat Ilgaz Meslek Yüksekokulu, Türkiye, Fırat Üniversitesi, Teknoloji Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye, Dumlupınar Üniversitesi, Mühendislik Fakültesi, Makine Mühendisliği Bölümü, Türkiye
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|