   Impact of Heat Treatment on Weight Loss During Combustion of Laminated Veneer Lumber (LVL)  
   
نویسنده perçin osman ,altunok mustafa
منبع journal of polytechnic - 2019 - دوره : 22 - شماره : 2 - صفحه:437 -442
چکیده    This study was performed to determine the effects of heat treatment on weight loss during combustion of the laminated wood materials produced from oriental beech (fagus orientalis l.), scotch pine (pinus sylvestris l.), sessile oak (quercus petraea l.), and poplar (populus nigra l.) veneers bonded with pvac-d4, pur and mf adhesives. for this aim, the weight loss during combustion of the test samples was determined according to astm e 160-50. the results of this study indicated that the weight loss percentage was the highest in poplar wood (89.17%), pvac-d4 adhesive (89.79%) and control samples (88.69%). in the interaction of the wood materials and type of adhesive, the highest value was measured in poplar+pur (90.93%), interaction of the wood materials and heat treatment in poplar + control samples (90.87%), in the interaction of the type of adhesive and heat treatment in pvac-d4 + 185 °c (91.10%). in the interaction of the wood material, type of adhesive and heat treatment temperature, the highest value was determined in laminated control poplar samples with pur adhesive (93%), while the lowest in laminated scotch pine samples with mf and heat-treated at 185 °c (81.83%). the use of laminated and heat-treated wood material in places where in high risk of fire, impregnation of wood material with fire-retardant compounds can be suggested.
کلیدواژه Heat treatment ,weight loss ,combustion ,adhesive ,wood material
آدرس necmettin erbakan university, faculty of fine arts, department of interior architecture and environmental design, Turkey, gazi university, technology faculty, department of wood products industrial engineering, Turkey
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved