   Corrosion Behavior of AA5754 Thin Sheets Welded with Cold Metal Transfer Method  
   
نویسنده durmuş hülya ,çömez nilay
منبع journal of polytechnic - 2018 - دوره : 21 - شماره : 4 - صفحه:907 -911
چکیده    Aa5754 aluminium alloy are widely used in outer and inner panels of automobiles. present study aimed to investigate the corrosion rate of cold metal transfer (cmt) welded 2 mm thick aa5754 sheets. welded sheets were produced with 73.97, 86.18, 108.99 j/mm heat input values using er5356 filler wire. effect of heat input on corrosion rate was determined by tafel extrapolation method. it was determined that corrosion rate increased with increasing heat input. corroded surfaces were viewed by sem. hardness test was applied and maximum hardness values were observed in weld metal.
کلیدواژه AA5754 ,CMT welding ,corrosion
آدرس manisa celal bayar üniversitesi, mühendislik fakültesi, metalurji ve malzeme mühendisliği bölümü, Turkey, manisa celal bayar üniversitesi, mühendislik fakültesi, metalurji ve malzeme mühendisliği bölümü, Turkey
پست الکترونیکی nilay.comez@cbu.edu.tr
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved