   The Physical Properties of Aluminium-7xxx Series Alloys Produced By Powder Metallurgy Method  
   
نویسنده acar ayşe nur ,ekşi abdul kadir ,ekicibil ahmet
منبع journal of polytechnic - 2018 - دوره : 21 - شماره : 2 - صفحه:341 -350
چکیده    Alumix-431 materials were prepared by cold and warm compaction method applying 350-400 mpa pressures at rt (room temperature) 50 and 80°c temperatures. the density measurements of materials were performed; the thermoelectric properties of materials were investigated at 5-300k under the he atmosphere, and the relationship between the measurements and sample properties was examined. the measurements of thermoelectric properties showed that maximum resistivity [alumix -431-1] and thermal conductivity [alumix -431-6] values were obtained 0.161ωm and 24.31w/km, respectively at 285-295k temperature ranges and minimum electrical resistivity and thermal conductivity values were obtained on alumix-431-6 and alumix-431-1 samples, respectively. it was observed that seebeck coefficient values varied mostly from negative sign to positive sign indicated dominate from carriers. the maximum figure of merit value was determined as 18.71×10-2; on the alumix-431-5 alloy at 96.904k.
کلیدواژه Cold and warm compaction ,powder metallurgy thermoelectric properties ,Al-7xxx alloys
آدرس university of çukurova, the faculty of ceyhan engineering, department of mechanical engineering, TURKEY, university of çukurova, thefaculty of engineering, department of mechanical engineering, TURKEY, university of çukurova, the faculty of arts and sciences, departmet of physics, turkey
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved