   Green Synthesis of Heteroatom Doped Graphene From Natural and Chemical Precursors For Oxygen Reduction Reaction  
نویسنده Sadegh Hassani Sedigheh ,Samiee Leila
منبع Journal Of Renewable Energy And Environment - 2021 - دوره : 8 - شماره : 4 - صفحه:1 -11
چکیده    In the present work, natural biomass and chemical materials were applied as the heteroatom resources for modifying the porous graphene (pg) structure by pyrolysis method at 900 °c. the physical and chemical characterizatons were performed by means of scanning electron microscopy (sem), brunauer–emmett–teller (bet), raman spectroscopy, n2 adsorption-desorption, and x-ray photo-electron spectroscopy (xps). furthemore, the behavior of the prepared materials was investigated by cyclic voltammetry (cv) and rotating disk electrode (rde). the obtained results indicated that doping of heteroatoms into the graphene framework was possible using a low-cost and environment-friendly biomass material as well as chemical sources. moreover, one-step quarternary and tersiary co-doped graphene could be acheived using natural biomass. the prepared electrocatalysts using grape leaves and sulfur trioxide pyridine complex exhibit higher electrocatalytic performance as exampled which conducted the electrocatalyst in 4e- pathway and showed high stability in methanol solutions during the process, confirming their considerable potential to oxygen reduction reaction (orr) as an electro-catalyst. moreover, the onset potential of gl300g-900 and gsp 900 (0.93 v vs rhe) is almost equal to the pt/c 20 wt % (0.99 v vs rhe). these optimal prepared cathodes (gl300g-900 and gsp 900) in the microbial fuel cell (mfc) test lead to considerable power densities of 31.5 mw m^-2 and 30.9.mw m^-2, which are close to 38.6 mw m^-2 for the pt/c 20 wt % cathode.
کلیدواژه Alkaline Fuel Cell ,Fuel Cell ,Graphene ,Electrocatalyst ,Natural Resources
آدرس Research Institute Of Petroleum Industry (Ripi), Catalysis Research Division, Iran, Research Institute Of Petroleum Industry (Ripi), Energy Technology Research Division, Iran
پست الکترونیکی leila.samiee83@gmail.com

Copyright 2015
Islamic World Science Citation Center
All Rights Reserved