   an investigation on the electrodeposition mechanism of ni-tio2 nanocomposite coatings  
   
نویسنده mohajeri soha ,dolati abolghassem ,ghorbani mohammad
منبع journal of ultrafine grained and nanostructured materials - 2016 - دوره : 49 - شماره : 2 - صفحه:51 -63
چکیده    In this research, a solmodified composite electrodeposition technique that combines the solgel method with the conventional electrodeposition process was utilized to deposit nitio2 nanocomposite coatings. cyclic voltammetry and chronoamperometry techniques were applied to study the influence of the tio2 sol concentration on the deposits’ electrochemical behavior. the results clearly showed that for higher sol concentrations, the onset potential of the nanocomposite deposition decreased compared to that of the pure ni. the scharifkerhill model was utilized at the initial times of deposition to study the nucleation mechanism. it was demonstrated that the nucleation mechanism of the nanocomposite at low overpotentials followed the progressive system, whereas at higher overpotentials it was found to be instantaneous with the threedimensional growth mechanism. the weight percentages of the codeposited tio2 nanoparticles were measured, and according to the results, the higher sol concentrations in the plating bath led to a higher tio2 nanoparticle content. the xrd results confirmed the presence of the anatase phase in the nitio2 nanocomposite coatings after 3 hours of heat treatment at 450°c. the surface morphology was studied by the scanning electron microscopy, confirming that the addition of higher sol concentrations refined the microstructure, particularly under higher deposition overpotentials. this was attributed to increased nucleation sites and the slow growth rate of the nuclei.
کلیدواژه electrodeposition ,ni-tio2 ,nanocomposite ,mechanism
آدرس sharif university of technology, department of materials science and engineering, ایران, sharif university of technology, department of materials science and engineering, ایران, sharif university of technology, department of materials science and engineering, ایران
پست الکترونیکی ghorbani@sharif.edu
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved