Martensite phase reversion-induced nano/ ultrafine grained AISI 304L stainless steel with magnificent mechanical properties

Austenitic stainless steels are extensively used in various applications requiring good corrosion resistance and formability. in the current study, the formation of nano/ ultrafine grained austenitic microstructure in a microalloyed aisi 304l stainless steel was investigated by the advanced thermomechanical process of reversion of strain-induced martensite. for this purpose, samples were subjected to heavy cold rolling to produce a nearly complete martensitic structure. subsequently, a wide range of annealing temperatures (600 to 800°c) and times (1 to 240 min) were employed to assess the reversion behavior and to find the best annealing condition for the production of the nano/ultrafine grained austenitic microstructure. microstructural characterizations have been performed using x-ray diffraction (xrd), scanning electron microscopy (sem), and magnetic measurement, whereas the mechanical properties were assessed by tensile and hardness tests. after thermomechanical treatment, a very fine austenitic structure was obtained, which was composed of nano sized grains of ~ 85 nm in an ultrafine grained matrix with an average grain size of 480 nm. this microstructure exhibited superior mechanical properties: high tensile strength of about 1280 mpa with a desirable elongation of about 41%, which can pave the way for the application of these sheets in the automotive industry.