Evaluating the Effect of Dentin Surface Pretreatment on the Static Contact Angle of A Drop of A Bonding Agent: An in Vitro Study

Introduction: the aim of this study was to investigate the effect of dentinal pretreatment on the static contact angle of a bonding agent as a measure of dentin surface wettability.materials &methods: twenty midcoronal dentin surfaces were prepared and randomly allocated to four groups (n=5) according to the priming solutions. all segments were etched with 35% phosphoric acid gel for 15 s, rinsed for 30 s and dried. each group was rehydrated with 10 &micro;l of distilled water, 0.2 % chlorhexidine, 70% ethanol and 5.25% sodium hypochlorite respectively and the excess solution was removed after 60 sec using an absorbent paper. using a micro syringe, a droplet of the adper single bond 2 was placed on each prepared surface. then the profile and the static contact angle of the droplet were analyzed with a videobased optical contact angle measuring system. the statistical analysis was performed using oneway anova and dunnett&rsquo;s t tests (p<0.05).results: there was a statistically significant difference between the water and sodium hypochlorite groups which indicates the negative effect sodium hypochlorite may have on dentinal surface energy. (p=0.013). the differences between the water and ethanol groups (p=0.168) and between the water and chlorhexidine groups (p=0.665) were not significant.conclusion: the use of 5.25% sodium hypochlorite as a priming solution in bonding procedure is not recommended. there is no improvement in dentinal surface wettability by using 70% ethanol or 0.2% chlorhexidine instead of water and the recommendation for use of any of the two should be based on other longterm or shortterm effects they may have on the bonding procedure.