Effect of Concentration of Hydrofluoric Acid and Etching Time on Microtensile Bond Strength of Zirconia-Reinforced Lithium Silicate Ceramics
|
|
|
|
|
نویسنده
|
Rostami Morteza ,Mokhtarpour Faraneh ,Alaghehmand Homayoon
|
منبع
|
Caspian Journal Of Dental Research - 2022 - دوره : 11 - شماره : 2 - صفحه:77 -84
|
|
|
چکیده
|
Introduction: etching the internal surface of ceramic restorations with hydrofluoric (hf) acid and silane is a well-accepted technique to enhance the bond strength. the aim of this study was to assess the effect of concentration of hydrofluoric acid and etching time on microtensile bond strength (μtbs) of zirconia-reinforced lithium silicate (zls) ceramics in 2021. materials & methods: this in vitro study was conducted on 8 celtra-duo ceramic blocks size 14 measuring 12×14×18 mm. each ceramic block was divided into three equal pieces by a cutting machine to obtain a total of 24 specimens. the specimens were randomly divided into 6 groups for etching with 5% and 10% hf acid for 30, 60, and 120 seconds. silane (clearfil porcelain activator) and bonding agent (clearfil se bond) were applied to the etched specimens. panavia f2 resin cement was applied on the surfaces and light-cured. the μtbs of resin cement to porcelain was measured by a universal testing machine. the mode of failure was determined under a stereomicroscope at x40 magnification. data were analyzed by oneand two-way anova (p<0.05). results: the mean μtbs of celtra-duo ceramics subjected to etching for 30, 60, and 120 seconds was not significantly different in the use of 5% and 10% hf acid concentrations (p>0.05). two-way anova showed that the effects of hf acid concentration and etching time, and their interaction effect were not significant on μtbs of cad/cam celtra-duo ceramics (p>0.05). the mode of failure was dominantly adhesive in both concentrations of 5% and 10% hf acid. no mixed failure occurred in both concentrations. conclusion: considering the non-significant difference in μtbs of ceramics subjected to different concentrations of hf acid for different times, the application of hf acid with lower concentration for a shorter period is recommended to prevent possible adverse effects on ceramic strength.
|
کلیدواژه
|
Ceramics ,Dentistry ,Hydrofluoric Acid ,Resin Cements
|
آدرس
|
Babol University Of Medical Sciences, Student Research Committee, Iran, Babol University Of Medical Sciences, Oral Health Research Center, Health Research Institute, Iran, Babol University Of Medical Sciences, Dental Materials Research Center, Health Research Institute, Iran
|
پست الکترونیکی
|
halaghemand@mubabol.ac.ir
|
|
|
|
|
|
|
|
|
بررسی اثر غلظتها و زمانهای مختلف اچ با اسید هیدروفلوئوریک بر استحکام باند ریزکششی سرامیک های لیتیوم سیلیکات تقویت شده با زیرکونیا (ZLS)
|
|
|
Authors
|
مختارپور فرانه ,رستمی مرتضی ,علاقمند همایون
|
Abstract
|
مقدمه: اچینگ سطح داخلی رستوریشنهای سرامیکی با اسید هیدروفلوئوریک و سایلن روش پذیرفته شده برای افزایش استحکام باند میباشد. این مطالعه با هدف تعیین اثر دو غلظت و سه زمان مختلف اچ با اسید هیدروفلوئوریک (HF) بر استحکام باند ریزکششی( micro;TBS) سرامیکهای لیتیوم سیلیکات تقویت شده با زیرکونیا (ZLS) در سال ۱۴۰۰ انجام گرفت.مواد و روشها: در این مطالعه آزمایشگاهی سرامیکهای سلترادیو به تعداد ۸ عدد به شماره ۱۴ با ابعاد mm ۱۸ ×۱۴ ×۱۲انتخاب شد. هر بلوک توسط دستگاه برش در عرض به ۳ قطعه مساوی تقسیم شد و ۲۴ نمونه آماده شد. سپس ۶ گروه سرامیکی توسط HF با غلظتهای ۵% و ۱۰% با زمانهای ۳۰، ۶۰ و ۱۲۰ ثانیه اچ شد. سطح نمونههای اچ شده به سایلن (Clearfill porcelain activator) و باندینگ (Clearfill SE bond) آغشته شد. سپس سمان رزینی (Panavia F.2) برروی سطوح زده شد و با نور کیور گردید. استحکام ریزکششی بین پرسلن و سمان رزینی با دستگاهMachine Universal Testing اندازهگیری شد.نوع شکست نیز با بزرگنمایی ۴۰ با استریومیکروسکوپ بررسی شد. دادهها توسط oneway ANOVA و Twoway ANOVA تجزیه و تحلیل شدند (0.05>P).یافته ها: میانگین micro;TBS سرامیکهای سلترادیو در غلظتهای ۵% و ۱۰% HF در زمانهای اچینگ ۳۰، ۶۰ و ۱۲۰ ثانیه مشابه بود و تفاوت معناداری نداشت (0.05<
|
Keywords
|
سرامیک ها، دندانپزشکی، اسید هیدروفلئوریک، سمان رزینی
|
|
|
|
|
|
|
|
|
|
|