   Electrical conduction and dielectric relaxation in p-type PVA/CuI polymer composite  
   
نویسنده Makled M.H. ,Sheha E. ,Shanap T.S. ,El-Mansy M.K.
منبع journal of advanced research - 2013 - دوره : 4 - شماره : 6 - صفحه:531 -538
چکیده    Pva/cui polymer composite samples have been prepared and subjected to characterizations using ft-ir spectroscopy, dsc analysis, ac spectroscopy and dc conduction. the ft-ir spectral analysis shows remarkable variation of the absorption peak positions whereas dsc illustrates a little decrease of both glass transition temperature, tg, and crystallization fraction, v, with increasing cui concentration. an increase of dc conductivity for pva/cui nano composite by increasing cui concentration is recoded up to 15 wt%, besides it obeys arhenuis plot with an activation energy in the range 0.54–1.32 ev. the frequency dependence of ac conductivity showed power law with an exponent 0.33 < s <0.69 which predicts hopping conduction mechanism. the frequency dependence of both dielectric permittivity and dielectric loss obeys debye dispersion relations in wide range of temperatures and frequency. significant values of dipole relaxation time obtained which are thermally activated with activation energies in the range 0.33–0.87 ev. a significant value of hopping distance in the range 3.4–1.2 nm is estimated in agreement with the value of bohr radius of the exciton.
کلیدواژه Polymer composite; CuI/PVA composite; dc Conductivity; FT-IR; DSC
آدرس Benha University, Faculty of Science, Physics Department, Egypt, Benha University, Faculty of Science, Physics Department, Egypt, Benha University, Faculty of Science, Physics Department, Egypt, Benha University, Faculty of Science, Physics Department, Egypt
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved