   effects of permeate pressure and feed flow rate on benzene dehydration by pervaporation  
   
نویسنده khatinzadeh ghasem ,mahdyarfar mohammad ,mehdizadeh ali ,esmailzadeh ali ,sattari abolfazl
منبع journal of petroleum science and technology - 2016 - دوره : 6 - شماره : 2 - صفحه:30 -36
چکیده    Membrane‐based pervaporation (pv) has attracted much attention in the dehydration of organic solvents. permeate pressure and feed flow rate are two important parameters, which affect membrane performance in pervaporation. the effects of these two parameters on the performance of a commercial poly (vinyl alcohol) membrane in the dehydration of benzene have been investigated in this work. the experiments have been carried out at a constant temperature of 60°c, and pressure and feed flow rate range from 1 to 20 mmhg and from 200 to 1200 ml/min respectively. the results indicate that variations in vacuum, especially in permeate pressures of less than 10 mmhg, greatly affect flux and selectivity so that water flux and separation factor increase from 0.98 to 2.63 (gr/hm2) and from 160 to 310 respectively by decreasing permeate pressure from 10 to 1 mmhg. furthermore, increasing flow rate improves membrane performance only at rates of below 1000 ml/min, and no changes are observed at higher feed flow rates.
کلیدواژه pervaporation ,dehydration ,permeate pressure ,benzene ,feed flow rate
آدرس research institute of petroleum industry(ripi), chemical polymeric and petrochemical technology development research division, iran, research institute of petroleum industry(ripi), chemical polymeric and petrochemical technology development research division, iran, research institute of petroleum industry(ripi), chemical polymeric and petrochemical technology development research division, iran, research institute of petroleum industry(ripi), chemical polymeric and petrochemical technology development research division, iran, research institute of petroleum industry(ripi), chemical polymeric and petrochemical technology development research division, iran
پست الکترونیکی sattaria@ripi.ir
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved