improving quality of municipal solid waste compost through mg-modified zeolite
|
|
|
|
|
|
|
|
نویسنده
|
taheri soudejani h. ,heidarpour m. ,shayannejad m. ,kazemian h. ,shariatmadari h. ,afuni m.
|
|
منبع
|
journal of agricultural science and technology - 2019 - دوره : 21 - شماره : 3 - صفحه:747 -760
|
|
چکیده
|
Developing materials to improve the efficiency of fertilizers and increase their performance is one of the main areas of research in the agricultural science. to the best of our knowledge, this is the first time that mgmodified zeolite is used for modification of composting process of urban organic solid waste. natural zeolite was clinoptilolite with a particle size smaller than 250 mu;m modified with mgcl2.6h2o salt. different ratios (i.e. 5, 10, and 15% , on a weight basis) of natural and/or mgmodified zeolite were used to modify the municipal solid waste (msw) compost. experimental results revealed that the ph of the final compost product with the mgmodified zeolite was effectively buffered at 7.7. furthermore, in comparison to the control treatment (without zeolite), the compost with natural and mgmodified zeolite showed 32.13 and 41.25% reduction in electrical conductivity, respectively. ammonium retention of the compost containing 15% natural and mgmodified zeolite was increased by 64.51 and 110.10%, respectively. metals mobility test of the matured composts also revealed that adding zeolite, especially the mgmodified zeolite, could decrease the mobility of cu, pb, zn, fe, ni, and mn metals. the most decrease in the mobility of metals was observed in cu, which was about 44.16 and 47.82%, in the compost with the natural and mgmodified zeolite, respectively.
|
|
کلیدواژه
|
ammonium retention ,composting ,conductivity reduction ,instead of composting ,metals mobility.
|
|
آدرس
|
isfahan university of technology, faculty of agriculture, department of water engineering, iran, isfahan university of technology, faculty of agriculture, department of water engineering, iran, isfahan university of technology, faculty of agriculture, department of water engineering, iran, university of northern british columbia (unbc), northern analytical lab services (nals), canada, university of northern british columbia (unbc), northern analytical lab services (nals), canada, isfahan university of technology, faculty of agriculture, department of soil science, iran
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
بهبود خصوصیات کمپوست زباله شهری با کاربرد زئولیت اصلاح شده با منیزیم
|
|
|
|
|
Authors
|
|
|
Abstract
|
توسعه مواد جدید برای بهبود راندمان استفاده از کود ها و افزایش عملکرد آن ها یکی از اهداف اصلی محققان در بخش کشاورزی است. مطالعات انجام شده نشان می دهد که این تحقیق برای اولین بار اثر زئولیت اصلاح شده با منیزیم را بر بهبود خصوصیات کمپوست زباله شهری بررسی می کند. زئولیت طبیعی از نوع کلینوپتیلولیت و با اندازه ذرات کمتر از 250 میکرون بود که با استفاده از نمک منیزیم کلرید اصلاح شد. مقادیر مختلفی از زئولیت طبیعی و اصلاح شده (5، 10 و 15 درصد وزنی) به منظور اصلاح کمپوست مورد استفاده قرار گرفت. نتایج مطالعه نشان داد با کاربرد کمپوست حاوی زئولیت اصلاح شده، pH کمپوست در انتهای دوره به طور موثری تا حدود 7/7 کاهش یافت. علاوه بر این، با کاربرد کمپوست حاوی زئولیت طبیعی و اصلاح شده، هدایت الکتریکی به ترتیب 13/32 و 25/41 درصد نسبت به تیمار شاهد (کمپوست بدون زئولیت) کاهش نشان داد. میزان نگهداشت آمونیوم با کاربرد کمپوست حاوی 15 درصد وزنی از زئولیت طبیعی و اصلاح شده 51/64 و 10/110 درصد افزایش یافت. با کاربرد زئولیت به ویژه زئولیت اصلاح شده تحرک فلزات Cu، Pb، Zn، Fe، Ni و Mnکاهش یافت. بیشترین میزان کاهش تحرک فلزات سنگین در فلز مس مشاهده شد. به گونه ای که با کاربرد کمپوست حاوی زئولیت طبیعی و اصلاح تحرک فلز مس به ترتیب 16/44 و 82/47 درصد نسبت به تیمار شاهدکاهش یافت.
|
|