Magnetic Properties and Structural Study of Ni-Co/Cu Multilayers Prepared by Electrodeposition Method

Ni-co/cu  multilayers  have  been  grown  by  electrodeposition method  from  a  single  electrolyte  (based  on  ni(so4).6h2o, co(so4).7h2o, cu(so4)  and h3bo3)  using  galvanostatic  control on  titanium  sublayers.  the  x-ray  diffraction  (xrd)  patterns confirmed  the  mult ilayer ed  structure  with  the  nanometer thicknesses.  also,  electron  diffraction  x-ray  (edx)    analysis confirmed the purity of deposited samples. the morphology of the samples  was  estimated  by  scanning  electron microscope  (sem). magnetoresistance  (mr) measurements were  carried  out  at  room temperature  for  the  ni-co/cu  multilayers  by  measuring  the resistivity  in  a magnetic  fields  varying  between  ±6koe  as  a function  of  the ni-co  and cu  layer  thicknesses;  (1  dcu(nm)  4 and  3  dni - cu (nm)  5) .   the  maximum  va lu e  of   giant magnetoresistance  (gmr) was  obtained  when  the ni-co  and cu thicknesses  were  4.0nm  and  4.0nm  respectively.  the  hysteresis loop  of  the  samples  at  room  temperature  was  studied  using  an alternating  gradient  force  magnetometer  (agfm).  finally,  the temperature  dependence  of  magnet izat ion  for  ni-co/cu multilayers;  (dni-cu(4nm)/dcu(2nm)  and  dni-cu(3nm)/dcu(3nm)) measured  by  faraday  balance  and  decreasing  the magnetization with  increasing  the  temperature  discussed  according  to  electron  scattering due to spin fluctuation.