Dodonaea viscosa (L.) Leaves extract as acid Corrosion inhibitor for mild steel - A Green approach

There is a growing trend to utilize plant extracts and pharmaceutical compounds as corrosion inhibitors. the inhibitive performance of extract of dodonaea viscosa leaves (dlve) on the corrosion of mild steel in 1m hcl and 0.5m h2so4 were studied using mass loss and electro chemical measurements. characterization of dlve wascarried out using gc-ms and ft-ir spectroscopy. results confirmed that the extract of dodonaea viscosa leaves (dvle) acts as an effective corrosion inhibitor in theacid environment. the inhibition efficiency increased with increase in concentration of the inhibitor and decreased with temperature. thermodynamic parameters revealed that the inhibition is through spontaneous adsorption of inhibitors onto the metal surface. potentiodynamic polarization and electrochemical impedance studies confirmed that the system follows mixed mode of inhibition. adsorbed film of inhibitor at metal /solution interface has been confirmed using reflectance fourier transform infrared spectroscopy. surface analysis by uv,ftir and sem confirmed the formation of protective layer on the mild steel (ms) surface. efforts were also taken to propose a suitable mechanism for the inhibition.