Glass-forming region,electrical and structural properties of BiPO4-NbOPO4-P2O5 (Bi2O3-Nb2O5-P2O5) glasses
|
|
|
|
|
نویسنده
|
laourayed m. ,el moudane m. ,guenbour a. ,tabyaoui m. ,bellaouchou a. ,ghanimi a. ,sabbar a.
|
منبع
|
journal of materials and environmental science - 2017 - دوره : 8 - شماره : 8 - صفحه:2932 -2939
|
چکیده
|
The glass forming region has been determined in the ternary system bipo4-nbopo4-p2o5. glasses with compositions xbipo4-(90-x)p2o5-10nbopo4 (20≤x≤35 mol%) and 20bipo4-(80-x)p2o5-xnbopo4 (5≤x≤30 mol%) were prepared. their physical,electrical and structural such as density,molar volume,ionic conductivity and ft-ir spectroscopy have been studied in order to understand the structural role of bi2o3 and nb2o5 in these glasses. the density of these glasses increases and their molar volume decreases with bi2o3 and nb2o5 contents. ft-ir study shows absorption peaks around 1200 cm-1,1100 cm-1,1000 cm-1,900 cm-1,780-730 cm-1,and 520-480 cm-1 corresponding to (po2)s,(po3)as,(po3)s,(p-o-p)as,(p-o-p)s and the bending vibration (δ) of p-o bonds,respectively. the ionic conductivity σ diminishes substantially with increasing concentration of either bi2o3 or nb2o5. the variation in σ is related to the decrease in o2- concentration,their mobilty and in the glass network polarization. a correlation between electrical and structurl properties of these glasses has been established. © 2017,university of mohammed 1er oujda morocco.
|
کلیدواژه
|
Density; Infrared spectroscopy; Ionic conductivity; Molar volume; Phosphate glasses
|
آدرس
|
laboratoire des matériaux,nanotechnologies et environnement,université mohammed,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco, laboratoire des matériaux,nanotechnologies et environnement,université mohammed,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco, laboratoire des matériaux,nanotechnologies et environnement,université mohammed,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco, laboratoire des matériaux,nanotechnologies et environnement,université mohammed,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco, laboratoire des matériaux,nanotechnologies et environnement,université mohammed,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco, laboratoire des matériaux,nanotechnologies et environnement,université mohammed,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco, equipe de physico-chimie des matériaux et nanomatériaux,université mohammed v,faculté des sciences,av. ibn battouta,b.p. 1014,rabat, Morocco
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|