evaluation of precipitation hardening heat treatment of ph 17-7 stainless steel spring
|
|
|
|
|
|
|
|
نویسنده
|
babakoohi ashrafi a. a. ,mohammadi h. ,habibolla zade a.
|
|
منبع
|
iranian journal of materials science and engineering - 2016 - دوره : 13 - شماره : 2 - صفحه:20 -28
|
|
چکیده
|
In this paper, the influence of heat treatment on ph17-7 stainless steel spring was evaluated. precipitation hardening phenomenon of ph 17-7 steel was evaluated in three stages. first, the spring constant changes with time and temperature was evaluated. second, the spring constant changes with respect to its original length at constant temperature and time with blocking (spring length after compression, 18 and 21 mm) were investigated. and finally, the spring heat treatment at 480 °c for 80 min and then holding at 230 °c in oil bath for 60 min without blocking were investigated. the results showed that the use of 18 mm block have large spring constant than 21 mm block. the optimal conditions (480 °c for 80 min) for this spring to reaching maximum spring constant were determined.
|
|
کلیدواژه
|
ph 17-7 stainless steel ,precipitation hardening ,spring constant ,blocking
|
|
آدرس
|
semnan university, metallurgical - material engineering department, ایران, amirkabir university of technology, mining and metallurgical engineering department, ایران, semnan university, metallurgical - material engineering department, ایران
|
|
پست الکترونیکی
|
ahabibolahzadeh@semnan.ac.ir
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|