the response of gfrp nanocomposites reinforced with functionalized swcnt under low velocity impact: experimental and ls-dyna simulation investigations

The low velocity impact (lvi) response of a pure and glass fiber reinforced polymer composites (gfrp)with 0.1, 0.3 and 0.5 wt.% of functionalized single-walled carbon nanotubes (swcnts) was experimentallyinvestigated. ls-dyna simulation was used to model the impact test of pure and incorporated gfrp with 0.3 wt.% of swcnt in order to compare experimental and numerical results of lvi tests. all tests were performed at twodifferent levels of energy. at 30j energy, the specimen containing 0.5 wt. % swcnt was completely destructed. theresults showed that the incorporated gfrp with 0.3 wt. % swcnt had the highest energy absorption and the backfacedamage area of this sample was smaller than other specimens. tem images from specimens were also analyzedand showed the incorporation of well-dispersed 0.1 and 0.3 wt. % of swcnt, while in specimens containing 0.5wt.% of cnt, tubes tended to be agglomerated causing a drop in the lvi response of the specimen. the contacttime of the impactor in numerical and experimental results was approximately equal. however, as the conditionsin numerical modeling are considered ideal, the maximum contact forces in ls dyna simulation results were higherthan the experimental results.