role of the electrostatic mechanism in the filtration process of nanofibers

The present study aims to investigate the role of the electrostatic mechanism in the filtration process ofpolyacrylonitrile nanofibers containing single-walled carbon nanotube. the nanofibers were fabricated viaelectrospinning using 16 wt% polyacrylonitrile polymer (pan) solution, single-wall carbon nanotubes (swnt) at aratio of 99:1 along with n and n-dimethylformamide solvents. initial filtration efficiency was tested as per iso29463:2011 standard inside a test rig. an electrostatic discharge test was performed via the chemical treatment ofthe filter media with isopropyl alcohol in accordance to en779 standard. mean initial filtration efficiency of thenanofiber media in the capturing of 100 nm and 200 nm particles were 95.92 ±2.74 and 97.26% ±1.11 respectively,while for particles between 80 to 250 nm, this was 96.73% ±2.74. the efficiency of the untreated media was 0.2 to1.2% higher than the pan/swnt media after electron discharge using isopropyl alcohol with an even biggerdifference being observed at lower particle size ranges. after treatment with isopropyl alcohol, the pressure drop ofthe filtration media was increased from 164.7 to 185.3 pa. the reduction in filtration efficiency observed after the electrostatic discharge test indicates that the electrical charge of the electrospun nanofibers is influential in itsinitial efficiency for removing the submicron particles.