effect of the la2o3 addition on thermal, microstructure and mechanical properties of mullite–zirconia composites

Mullite -zirconia composites were prepared using lanthanum oxide (la2o3) additive which three different mole ratio by the reaction sintering (rs) route of alumina, kaolinite and zircon. starting materials were planetary milled, shaped into pellets and bars and sintered in the temperature range of 1450 -1550 0c with 5 h soaking at peak temperature. in this work, the mullitezirconia composites were characterized by thermal expansion coefficient, physical, microstructures and mechanical properties. the xrd method were employed for determining the crystalline phase composition of these composites. microstructure of the composites was examined by sem. zro2 takes part in both the intergranular as well as intragranular positions. however, intragranular zirconias are much smaller compared to intergranular zirconias.