THE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
|
|
|
|
|
|
|
|
نویسنده
|
Ozve Aminian M. ,Kharazi Y. ,Hedjazi J.
|
|
منبع
|
iranian journal of materials science and engineering - 2009 - دوره : 6 - شماره : 3 - صفحه:21 -28
|
|
چکیده
|
In this research, the oxidation behaviour of high aluminum heat resistant steel (%25cr,%20ni,%8al) hasbeen evaluated at the temperature range of (1000-1300ºc).the results showed that there was no countinous healinglayer on the surface of the alloy when al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.by increasing the aluminum amount to %8, only al oxide formed due to decreasing carbon potential of thealloy,homogenity of elemental concentration in matrix and no diffusion of oxygen through oxide–metalinterface,therefore it has superior oxidation resistance. meanwhile,oxidation tests showed that the weight gain of thesteel at high temperature oxidation even at 1300ºc was too low.
|
|
کلیدواژه
|
High Aluminum steel ,Heat resistant steel ,Oxidation resistance ,Protective -Al2O3.
|
|
آدرس
|
iran university of science and technology, ایران, iran university of science and technology, School of Metallurgy and Materials Engineering, ایران, iran university of science and technology, School of Metallurgy and Materials Engineering, ایران
|
|
پست الکترونیکی
|
magmaaminian@yahoo.com
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|