   The Effect of Quenching Media and Annealing Temperature on Graphitization Transformation Kinetic of Ck100 Tool Steel  
   
نویسنده Rounaghi .S.A ,Kiani-Rashid .A.R
منبع International Journal Of Iron And Steel Society Of Iran - 2011 - دوره : 8 - شماره : 1 - صفحه:34 -38
چکیده    In this research, graphitization transformation of a commercial hypereutectoid steel called ck100 was studiedby the dilatometric experiments at the range of 600 – 700 °c from prior martensitic structure. also the effect ofquenching media on the initial graphitization time and completion of transformation has been discussed. also,graphitization transition from the different prior microstructures was studied using microscopic observations.analyzing dilatometric data acquisitions confirmed good following results from johnson–mehl–avrami equation.by calculating avrami exponent, following of transformation kinetic from diffusion controlled nucleation andgrowth was resulted. also, the minimum time for completion graphitization transformation was concluded about45 hrs relative to the water quenched specimen after annealing at 670 °c.
کلیدواژه Graphitization ,Ck100 ,Microstructure ,Martensite
آدرس دانشگاه فردوسی مشهد, Department Of Materials Engineering, Ferdowsi University Of Mashhad, Mashhad, Iran, ایران, دانشگاه فردوسی مشهد, Department Of Materials Engineering, Ferdowsi University Of Mashhad, Mashhad, Iran, ایران
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved