Morphological and Physical Study of La0.7Sr0.3Co0.2Fe0.8O3-δ (LSCF 7328) Flat Membranes Modified by Polyethylene Glycol (PEG)

The aim of this work is to study the effect of polyethylene glycol (peg) on the modification of microstructure formation correlated with the mechanical strength properties of perovskitebased membrane in form of a flat sheet. lscf 7328 flat membrane was potentially promoted as an oxygen separator and catalyst for partial oxidation of methane reaction at high temperature. in this study, the phase-inversion followed by sintering process was used as the membrane fabrication method using varied peg concentration of 0.55, 1.00, and 3.00 wt% with different molecular weight, i.e., peg 300, 600, 1500, and 4000 da for each peg concentration. the result of morphology observation shows that almost every membrane hasthe asymmetric structure with finger-like pores and thin dense layer. increasing peg concentration as well as molecular weight increases pore size and affects on porosity, pore's volume, and physical properties of membrane. the largest pore size, pore volume and porosity of the membrane after sintering were found in the addition of 3.00% peg 4000 (da) additive with the value of 110.45 μm, 81.34 ml.g-1 and 120.6%, respectively. in addition, the mechanical properties of membrane were tested using the vickers micro hardness method with the greatest value found in the addition of 3.00% peg 1500 (da) additive with the value of 13.58 hv and the lowest is 3.00% peg 4000 (da) with the value of 1.2 hv.