   Synthesis and Preparation of Asymmetric PSf/ZIF-8 Mixed Matrix Membrane for CO2/CH4 Separation  
   
نویسنده Nordin Nik Abdul Hadi Md ,Ismail Ahmad Fauzi ,Mustafa Azeman
منبع jurnal teknologi - 2014 - دوره : 69 - شماره : 9 - صفحه:73 -76
چکیده    Utilizing nano-size filler into polymer matrix would overcome challenges in developing mmm by providing good dispersion in polymer matrix, high contact polymer-filler even at low filler loading. asymmetric neat polysulfone (psf) and psf/zeolitic imidazole framework-8 (psf/zif-8) mixed matrix membrane was prepared using dry/wet inversion method. membrane prepared was coated with 3wt% of polydimethylsiloxane (pdms) in n-hexane and undergoes heat treatment. the membranes was characterized using x-ray diffraction (xrd), thermagravimetric analysis (tga), differential scanning calorimetry (dsc), and gas permeation test at 4 bar. xrd pattern revealed that zif-8 was successfully synthesis with crystal size around 73nm. lowered membrane tg after embodiment of zif-8 suggests that additional free volume form, while thermal stability up to 350°c related to zif-8 stability. neat psf prepared shows co2 permeance at 4.97 gpu with co2/ch4 selectivity at 7.52. interestingly, incorporation of zif-8 showing improvement for both co2 permeance and co2/ch4 selectivity up to 51% and 47% respectively. thus, employing nano zif-8 as filler into psf matrix has resultant promising membrane for co2/ch4 separation.
کلیدواژه Mixed matrix membrane; PSf/ZIF-8; CO2/CH4 separation
آدرس Universiti Teknologi Malaysia, Advance Membrane Technology Research Centre (AMTEC), Faculty of Petroleum and Renewable Energy Engineering, Malaysia, Universiti Teknologi Malaysia, Advance Membrane Technology Research Centre (AMTEC), Faculty of Petroleum and Renewable Energy Engineering, Malaysia, Universiti Teknologi Malaysia, Advance Membrane Technology Research Centre (AMTEC), Faculty of Petroleum and Renewable Energy Engineering, Malaysia
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved