   Assessment of Green Inhibitor on the Crystal Structures of Carbonated Concrete  
   
نویسنده Abdulrahman A. S. ,Ismail Mohammad
منبع jurnal teknologi - 2014 - دوره : 69 - شماره : 3 - صفحه:1 -9
چکیده    The present paper involves studies of inhibitors on carbonation depth and carboaluminates of concrete which was exposed to accelerated carbonation. three inhibitors used were; calcium nitrite, ethanolamine and eco-friendly green bambusa arundinacea. concrete mix was designed to be 30 mpa with 0.45 w/c ratios which was chloride contaminated by 1.5% weight of cement content from analytical grade of magnesium chloride salt. inhibitors additions were 2% and 4% weight of cement content. the results show that bambusa arundinacea inhibitor distinctively shows lowest level of carbonation. this developed hydrophobic green inhibitor characteristics was able to form impermeable barrier against co2 gas. additionally, hemicarboaluminate phases appears at hydration in calcite-containing portland cement, even in the presence of two inhibitors (calcium nitrite and ethanolamine) which gradually converted to monocarboaluminate. whereas, bambusa arundinacea inhibitor causes the saturation of portlandite that maintained ca/si ratio above 1.65 and c-s-h remain unaffected by carbonation.
کلیدواژه Concrete; carbonation; inhibitors; durability; AFm phases
آدرس Federal University of Technology, Department of Mechanical Engineering, Nigeria, Universiti Teknologi Malaysia, Faculty of Civil Engineering, UTM Construction Research Centre, Malaysia
 
     
   
Authors
  
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved