Microstructural Properties of Semisolid Welded Joints for AISI D2 Tool Steel
|
|
|
|
|
|
|
|
نویسنده
|
Mohammed M.N. ,Omar M.Z. ,Syarif J. ,Sajuri Z. ,Salleh M.S. ,Alhawari K.S.
|
|
منبع
|
journal of engineering - 2014 - دوره : 26 - - کد همایش: - صفحه:31 -34
|
|
چکیده
|
The aim of this study is to investigate experimentally the microstructural evolution of the joints using ledeburitic aisi d2 tool steel parts. the application of a new process of the semisolid joining of two parts of aisi d2 cold-work tool steel is proposed using a partial remelting method. samples were heated in an argon atmosphere up to 1300°c and held for 10 minutes. metallographic analyses along the joint interface showed a smooth transition from one to the other and neither oxides nor microcracking was observed. the current work successfully confi rmed that avoidance of a dendritic microstructure in the semisolid joined zone and high bonding quality components can be achieved without the need for force or complex equipment when compared to conventional welding processes.
|
|
کلیدواژه
|
Thixo-joining; direct partial re-melting; cold-work tool steel
|
|
آدرس
|
Universiti Kebangsaan Malaysia, Faculty of Engineering and Built Environment, Department of Mechanical and Materials Engineering, Malaysia, Universiti Kebangsaan Malaysia, Faculty of Engineering and Built Environment, Department of Mechanical and Materials Engineering, Malaysia, Universiti Kebangsaan Malaysia, Faculty of Engineering and Built Environment, Department of Mechanical and Materials Engineering, Malaysia, Universiti Kebangsaan Malaysia, Faculty of Engineering and Built Environment, Department of Mechanical and Materials Engineering, Malaysia, Universiti Kebangsaan Malaysia, Faculty of Engineering and Built Environment, Department of Mechanical and Materials Engineering, Malaysia, Universiti Kebangsaan Malaysia, Faculty of Engineering and Built Environment, Department of Mechanical and Materials Engineering, Malaysia
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|