Electrodeposition of Nano Hydroxyapatite Coating on Biodegradable Mg-Zn Scaffold
|
|
|
|
|
نویسنده
|
Seyedraoufi Z. S. ,Mirdamadi S. ,Rastegari S.
|
منبع
|
International Journal Of Engineering - 2014 - دوره : 27 - شماره : 6 - صفحه:939 -944
|
|
|
چکیده
|
In this research, porous magnesium-zinc scaffolds were prepared by powder metallurgical process and nano hydroxyapatite (hap) coating on the mg-3zn (wt.%) scaffold was prepared by pulseelectrodeposition and alkali treatment processes to improve the corrosion resistance of the scaffold. the results indicated the as-deposited coating consists of hap, dcpd and ocp with needle-like and plate-like structures and the post-treated coating was composed of needle-like particles of nano hap that developed almost perpendicularly to the substrate. electrochemical tests showed that the corrosion potential of scaffold significantly increased from -1.475 to -1.365 v and the corrosion current density reduced 1.5-fold in comparison to the scaffold modified by nano hydroxyapatite coating.
|
کلیدواژه
|
Biodegradable Mg–Zn Scaffold ,Nano Hydroxyapatite Coating ,Electrodeposition ,Corrosion Resistance
|
آدرس
|
Iran University Of Science And Technology, School Of Metallurgy And Materials Engineering, Center Of Excellence For High Strength Alloys Technology ( Cehsat), ایران, Iran University Of Science And Technology, School Of Metallurgy And Materials Engineering, Center Of Excellence For High Strength Alloys Technology ( Cehsat), ایران, Iran University Of Science And Technology, School Of Metallurgy And Materials Engineering, Center Of Excellence For High Strength Alloys Technology ( Cehsat), ایران
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|