metallurgical and mechanical behavior of aisi 316 aisi 304 during friction welding process

Present study focuses on the microstructural and mechanical behavior effect of friction time for similar (aisi 316aisi 316 and aisi 304aisi 304) and dissimilar (aisi 304aisi 316) joint during continuous drive friction welding. the welding carried out with different friction time: 6.5, 8.5 and 10 s while kept all other conditions constant. the effect of that time on the strength, structural and behavior of welded metals was investigated by energy dispersive spectroscopy (edax), scanning electron microscope (sem), microhardness and tensile test. the obtained results illustrated that the friction time extended was responsible on some harmful mechanical and microstructural properties of the welded joint. therefore, increasing in friction time is led to reduce of ultimate tensile strength (uts), reduce of ductility, increasing in level of microhardness and larger hpdz, that was clearly observed in similar joint (aisi 316aisi 316 and aisi 304aisi 304).