   Effect of Welding Heat Input on the Intermetallic Compound Layer and Mechanical Properties in Arc Welding-Brazing Dissimilar Joining of Aluminum Alloy To Galvanized Steel  
   
نویسنده Zarouni M. ,Eslami-Farsani R.
منبع International Journal Of Engineering - 2016 - دوره : 29 - شماره : 5 - صفحه:669 -676
چکیده    The effect of weld heat input on the formation of intermetallic compound (imcs) layer during arc welding–brazing of aluminium and steel dissimilar alloys was investigated through both finite element method (fem) numerical simulations and experimental measurements. the results of fem analysis as well as welding experiments indicated that increasing weld heat input increases the thickness of imcs layer. the thickness of imcs layers, as calculated from fem simulations, was approximately equal to that measured from microstructural images in the range of 2-6 μm. the tensile strength of arc welding–brazing joints was dependent on the thickness of imcs layer and spreading of molten weld metal on the surfaces of steel sheet. the highest mechanical strength of 120 mpa was obtained in the optimized heat input of 420 j/mm. the presence of the si element in the al-5si filler metal led to imcs layer with the composition of fe(al,si)3 phase in side of the steel and al7.2fe1.6si phase in side of the weld seam.
کلیدواژه Arc Welding-Brazing ,Numerical Simulation ,Dissimilar Alloy ,Intermetallic Compound Layer
آدرس K. N. Toosi University Of Technology, Faculty Of Materials Science And Engineering, ایران, K. N. Toosi University Of Technology, Faculty Of Materials Science And Engineering, ایران
 
 

Copyright 2015
Islamic World Science Citation Center
All Rights Reserved