Effect of Post-Cure Time on Residual Stress Distribution in Carbon/Epoxy Laminated Composites

This research investigates the effect of post-cure time on residual stresses in laminated composites. laminated composites were made of t300 carbon fibers and epoxy resin. the post-cure process was carried out at the constant temperature of 120 °c for 6 and 12 hours for two specimens. the slitting method was employed to determine through-thickness residual stress distribution of the composite laminates. the results of experiment indicates that increasing the post-cure time leads to the reduction of maximum residual stress, as well as the uniformity of the residual stress distribution in laminated composites. therefore, increasing the post-cure time is an effective way of reducing the destructive effects of residual stresses in laminated composites.