corrosion inhibition effect of ester containing cationic gemini surfactants on low carbon steel

Α, ωalkanebis(nmyristoyloxyethyln, ndimethyl)diammonium bromide were synthesized and confirmed by ftir, ftraman and 1hnmr spectroscopy. surface tensions were measured by sigma 70 and conductivity meter ec470c. critical micelle concentration values were 2.70×104∼3.05×104 mol/l. the krafft points were measured at 39.1 ~ 43.2℃. their inhibition effects on the corrosion of low carbon steel were tested by the weight loss method in hydrochloric acid. the corrosion inhibition capacity of synthesized cationic gemini surfactant was 24.8% at 1 x 107mol/l concentration. corrosion inhibition efficiency has increased by 93.8% after the concentration was increased to 1 x 104mol/l. as a result, these surfactants are expected to be applied as corrosion inhibitors.