potential use of algerian metallurgical slag in the manufacture of sanitary ceramic bodies and its effect on the physical-mechanical and structural properties
|
|
|
|
|
|
|
|
نویسنده
|
boulaiche khaled ,boudeghdegh kamel ,roula abdelmalek ,alioui hichem ,oualid mahieddine hamdi
|
|
منبع
|
iranian journal of chemistry and chemical engineering - 2023 - دوره : 42 - شماره : 2 - صفحه:461 -471
|
|
چکیده
|
A study of the partial substitution of feldspar by blast furnace slag (bfs) and its effects on the properties of sanitary ceramics, has been carried out. characterization of rheological behavior, thermal, structural, physical, and mechanical properties of fired sanitary-ware bodies, show that 10wt. % is the optimal value for bfs in the formulation of sanitary ceramic. drx, sem, and ft-ir analyses confirmed that the starting crystalline phases (quartz and mullite), with the gradual appearance of anorthite, allow a non-negligible improvement in flexural strength (33 to 38 mpa), and a reduction in water absorption (0.35 to 0.10 %). from dta/tg data, a little change in weight loss during the firing process (8.83 to 9.66 wt. %), was recorded. the na-electrolytes with a mass ratio na2co3/ na2sio3 = 1.5, and a combined mass percentage (0.375 wt. %), are found to give the optimum values for good quality sanitary ceramic slip.
|
|
کلیدواژه
|
bfs ,physical properties ,flexural strength ,sanitary ceramic bodies
|
|
آدرس
|
msby jijel university, faculty of sciences and technology, laboratory of applied energetics and materials (laem), process engineering department, algeria, msby jijel university, faculty of sciences and technology, laboratory of applied energetics and materials (laem), process engineering department, algeria, msby jijel university, faculty of sciences and technology, laboratory of interactions material-environment (lime), process engineering department, algeria, msby jijel university, faculty of sciences and technology, laboratory of civil engineering and environment (lcee), civil engineering department, algeria, university of science and technology houari boumediene (usthb), faculty of civil engineering, laboratory of environment, water geomechanics and structures (leego), algeria
|
|
پست الکترونیکی
|
ohamdi@usthb.dz
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|