synthesis and characterization of fe-al2o3 nanoparticles prepared by coprecipitation method
|
|
|
|
|
|
|
|
نویسنده
|
farahmandjou majid ,khodadadi abolfazl ,yaghoubi mojtaba ,khodadadi shahaab
|
|
منبع
|
iranian journal of chemistry and chemical engineering - 2021 - دوره : 40 - شماره : 3 - صفحه:725 -730
|
|
چکیده
|
In this study, iron-doped alumina (fe-al2o3) nanoparticles (nps) containing 2 mol%, 4 mol%, and 6 mol% iron impurities were fabricated by the co-precipitation method in the presence of al2(so4)3.9h2o and fe2(so4)3.9h2o precursors. the prepared nanoparticles were heated at 1000 oc to study their physicochemical properties. the xrd results pointed out the multiphase for the samples. the morphological results revealed that the uniformity increased by increasing iron atoms rate. tem analysis revealed that the particle with a size of 40 nm was obtained for 4% of the sample. the results of ft-ir analysis indicated that when the 2% impurity increases the alo4 tetrahedra and alo6 octahedral vibrational bond grow.
|
|
کلیدواژه
|
fe-doped al2o3; nanocrystals; coprecipitation method; optical properties; catalyst; ceramics materials
|
|
آدرس
|
islamic azad university, varamin pishva branch, department of physics, iran, islamis azad university, tehran north branch, department of physics, iran, islamic azad university, ayatollah amoli branch, departments of physics, iran, islamic azad university, tehran medical branch, department of science, iran
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|